Goynta-beegyada uu nidaamka
1. Description of awoodda processing
wax |
dhumucdiisuna |
gaaska darran |
carbon steel |
<12mm |
ogsijiin |
Bir daxal laheyn |
<6mm |
nitrogen |
Aluminum daawaha |
<2mm |
nitrogen |
sheet galvanized |
<4mm |
ogsijiin |
2.Part argument habka
ku xiran tahay content carbon mid ah waxyaabaha la soo, xawaaraha gaar ah kala duwanaan karaan (tixraac oo kaliya)
wax |
dhumucdiisuna |
gaaska |
xawaaraha Jarida |
|
0.5 |
nitrogen |
小于 24 / min |
Bir daxal laheyn |
1 |
nitrogen |
16.8 ~ 21 / min |
2 |
nitrogen |
5.4 ~ 7.2m / min |
|
3 |
nitrogen |
2.1 ~ 3 / min |
|
4 |
nitrogen |
0.9 ~ 1.5 / min |
|
5 |
nitrogen |
0.6 ~ 0.9m / min |
|
carbon steel |
1 |
ogsijiin |
15 ~ 18 / min |
2 |
ogsijiin |
5.1 ~ 6 / min |
|
3 |
ogsijiin |
3,48 ~ 4.2 / min |
|
4 |
ogsijiin |
2,28 ~ 2.7 / min |
|
5 |
ogsijiin |
1,98 ~ 2.1m / min |
|
6 |
ogsijiin |
1.2 ~ 1.8m / min |
|
8 |
ogsijiin |
0.9 ~ 1.08m / min |
|
10 |
ogsijiin |
0.6 ~ 0.72m / min |
|
Aluminum daawaha |
1.2 |
nitrogen |
5 / min |
2.0 |
nitrogen |
3 / min |
|
sheet galvanized |
2 |
nitrogen |
5 / min |
naxaas |
2 |
nitrogen |
4-7m / min |